Flux Cored Welding Wire, Aws A5.20 E71t-1c 1.2mm 15kg/Spool

Model NO.: AWS A5.20 E71T-1C
Trademark: TOKO
Transport Package: 10kg/Roll, 15kg/Roll, 20kg/Roll
Specification: approved by: ABS, LR, BV, GL, DNV, KR, CCS
Origin: China
HS Code: 83111200
Model NO.: AWS A5.20 E71T-1C
Trademark: TOKO
Transport Package: 10kg/Roll, 15kg/Roll, 20kg/Roll
Specification: approved by: ABS, LR, BV, GL, DNV, KR, CCS
Origin: China
HS Code: 83111200
Flux Cored Welding Wire, Aws A5.20 E71t-1c 1.2mm 15kg/Spool
TOKO AWS A5.20 E71T-1C is formulated to deposit x-ray quality welds in flat, vertical up, horizontal, or overhead positions. E71T-1C is designed for welding low carbon and mild steel, structural and pressure vessel grades. E71T-1C flux core ingredients produce a fast freezing slag that facilitates out of position welds. Bead contour is flat to slightly convex. Slag is easy to remove and low spatter provides easy post weld cleaning.

Instruction

1. Gas- Shielded:Above 99.98% CO2

2. When welding, the gas flow rate shoule keep between 20L/min and 25L/min

3.The oil stains and rust on the welding should be cleared away.

Chemical Composition of Deposited Metal

  C Mn Si P S
Case 0.052 1.4 0.42 0.019 0.011
(W/ CO2)
Standard ≤0.18 ≤1.75 ≤0.90 ≤0.03 ≤0.03
( AWS E71T-1)

Machanical Properties of Deposited Metal

  YP Rel/ Mpa Tensile Strength/ Mpa Elongation % Impact Value
Case 505 570 28 -20°C/ 120
(W/ CO2)
Standard ≥375 490-660 22 27
( AWS E71T-1)

Reference Welding Parameter (DC+)

Specification 1.2 1.4 1.6
( Diameter Size mm)
Volt 23-30 24-36 25-40
Amp 150-300 170-360 200-400
mm 15-25 15-25 20-30
L/min 20-25 20-25 20-25
 

Application

Shipbuilding, Offshore, bridge, pressure vessal and general fabrications etc.

Flux Cored Welding Wire, Aws A5.20 E71t-1c 1.2mm 15kg/Spool
Diameter: 0.8mm / 0.9mm/ 1.0mm / 1.2mm / 1.6mm / 2.0mm / 2.4mm
Shipping approval: ABS, LR, BV, GL, DNV, KR, CCS 

Flux Cored Welding Wire, Aws A5.20 E71t-1c 1.2mm 15kg/Spool
Flux Cored Welding Wire, Aws A5.20 E71t-1c 1.2mm 15kg/Spool
Welding Slags are 100% removed Automatically......TOKO brand Flux Cored Welding Wire E71T-1 1.2MM 
Flux Cored Welding Wire, Aws A5.20 E71t-1c 1.2mm 15kg/Spool

  Flux Cored Welding Wire, Aws A5.20 E71t-1c 1.2mm 15kg/Spool
TOKO AWS A5.20 E71T-1C is formulated to deposit x-ray quality welds in flat, vertical up, horizontal, or overhead positions. E71T-1C is designed for welding low carbon and mild steel, structural and pressure vessel grades. E71T-1C flux core ingredients produce a fast freezing slag that facilitates out of position welds. Bead contour is flat to slightly convex. Slag is easy to remove and low spatter provides easy post weld cleaning.

Instruction

1. Gas- Shielded:Above 99.98% CO2

2. When welding, the gas flow rate shoule keep between 20L/min and 25L/min

3.The oil stains and rust on the welding should be cleared away.

Chemical Composition of Deposited Metal

  C Mn Si P S
Case 0.052 1.4 0.42 0.019 0.011
(W/ CO2)
Standard ≤0.18 ≤1.75 ≤0.90 ≤0.03 ≤0.03
( AWS E71T-1)

Machanical Properties of Deposited Metal

  YP Rel/ Mpa Tensile Strength/ Mpa Elongation % Impact Value
Case 505 570 28 -20°C/ 120
(W/ CO2)
Standard ≥375 490-660 22 27
( AWS E71T-1)

Reference Welding Parameter (DC+)

Specification 1.2 1.4 1.6
( Diameter Size mm)
Volt 23-30 24-36 25-40
Amp 150-300 170-360 200-400
mm 15-25 15-25 20-30
L/min 20-25 20-25 20-25
 

Application

Shipbuilding, Offshore, bridge, pressure vessal and general fabrications etc.

Flux Cored Welding Wire, Aws A5.20 E71t-1c 1.2mm 15kg/Spool
Diameter: 0.8mm / 0.9mm/ 1.0mm / 1.2mm / 1.6mm / 2.0mm / 2.4mm
Shipping approval: ABS, LR, BV, GL, DNV, KR, CCS 

Flux Cored Welding Wire, Aws A5.20 E71t-1c 1.2mm 15kg/Spool
Flux Cored Welding Wire, Aws A5.20 E71t-1c 1.2mm 15kg/Spool
Welding Slags are 100% removed Automatically......TOKO brand Flux Cored Welding Wire E71T-1 1.2MM 
Flux Cored Welding Wire, Aws A5.20 E71t-1c 1.2mm 15kg/Spool

 

EDM Graphite

EDM graphite, also known as graphite block for EDM, is a new type of material, which is now more and more widely used in the precision mold processing industry. At present, in mold processing plants in developed European countries, more than 90% of mold processing electrode materials are graphite. Copper, the once dominant electrode material, has almost lost its advantages compared with graphite electrodes.
83
Our isostatic graphite and Molded Graphite were tested at the National Electrical Carbon Products Quality Supervision and Inspection Center. The main physical and chemical performance index as follows: the compressive strength--125 mpa, shore hardness -- 65 degrees, resistivity --12 mu Ω m. At the same time, the 10μm,8μm,6μm,4μm products have already began Large-scale production,.and unanimously acknowledged by customers. The 2μm,1μm graphite products are under trial. Our company high quality of isostatic pressing special graphite yield above 90%, far ahead of industry the yield of 70%, the first in the country.

Company main products:

1.Isostatic Graphite Block

2.Molded graphite block

3.Graphite rod

4.Graphite tube

5.Graphite plate

6.Graphite Parts

7.Graphite crucible

Customized High Pure and density graphite products/graphite block for EDM

Edm Graphite,Graphite Block For Edm,Edm Graphite Electrodes,Isostatic Graphite Column

CARBONS TECH&CREATION(HENAN) INDUSTRY CO.,LTD , https://www.kycarbon.com

Posted on